Dental zirconia blocks are an essential component in the fabrication of dental restorations, such as dental crowns, bridges, and implant-supported structures.
These blocks are made from high-quality zirconia material, which is known for its durability, biocompatibility, and aesthetic properties.
HT White CAD/CAM Zirconia Block
Safety - Good biocompatibility 丨CAM - Nesting friendly 丨Transition - No Layer lines
HT/ST/SHT/UT/3D/4D-ML Sintering
Max Heating rate:10°C per minute
Final temperature:1500℃-1550℃，1530℃ is best
Holding time at final temperature:130 min
Cooling should be done without temperature control in closde furnace
Never open the furnace before it has reached a temperature of less than 80°C to avoid thermal shocks
| Product Type | Translucency | Strength | Colors | Sintering Temperature |
| 4D Pro-Multilayer | 43-57% | 700-1000MPa | White,16 vita, BL1-4 | 1530℃ |
| 3D Pro-Multilayer | 43-55% | 800-1200MPa | White,16 cita, BL1-4 | 1530℃ |
| SHT-C | 49% | 900MPa | White,A1,A2,A3,B1,B2 | 1530℃ |
| SHT-ML | 49% | 900MPa | A1,A2,A3,B1,B2,BL1-4 | 1530℃ |
| ST-C | 43% | 1200MPa | White,16 vita | 1530℃ |
| ST-ML | 43% | 1200MPa | 16 vita | 1530℃ |
| UT-C | 57% | 600MPa | White,16 vita | 1530℃ |
| UT-ML | 57% | 600MPa | 16 vita | 1530℃ |
| HT | 40% | 1350MPa | White | 1530℃ |