SHT Multilayer
CAD/CAM Zirconia Block
Safety: Good biocompatibility
CAM - Nesting friendly
Transition - No Layer lines
SHT Multilayer CAD/CAM Zirconia Block
Safety: Good biocompatibility 丨 CAM - Nesting friendly 丨 Transition - No Layer lines
HT/ST/SHT/UT/3D/4D-ML Sintering
Max Heating rate: 10C per minute
Final temperature:1500℃-1550℃，1530°℃ is best
Holding time at final temperature:130 min
Cooling should be done without temperature control in closde furnace
Never open the furnace before it has reached a temperature of less than 80℃ to avoid thermal shocks
| Product type | Translucency | Strength | Color | Sintering temperature |
| 4D-Pro Muitilayer | 43-57% | 700-1000MPa | White,16 VITA,BL1-4 | 1530℃ |
| 3D-Pro Muitilayer | 43-55% | 800-1200MPa | White,16 VITA,BL1-4 | 1530℃ |
| SHT-C | 49% | 900MPa | White, A1, A2,A3, B1,B2 | 1530℃ |
| SHT-ML | 49% | 900MPa | A1,A2,A3,B1,B2,BL1-4 | 1530℃ |
| ST | 43% | 1200MPa | White,16 VITA | 1530℃ |
| ST-ML | 43% | 1200MPa | 16 VITA | 1530℃ |
| UT | 57% | 600MPa | White,16 VITA | 1530℃ |
| UT-ML | 57% | 600MPa | 16 VITA | 1530℃ |
| HT | 40% | 1350MPa | White | 1530℃ |